Leaded Bronzes
-
10
-
CuPb10Sn10
Norms CC495K, EN 1982, GAM-MM12
Production technique Continous casting, Centrifugal casting
Chemical composition | Mechanical characteristics | ||||||||||||||||||||||||||||
Cu | Sn | Pb | Zn | P | Al | Ni | Fe | Mn | Si | Other | Rm | Rp | A% | HB | Density | ||||||||||||||
Reste | 8,0-11 | 9,0-11 | ≤2 | ≤0,1 | ≤0,01 | ≤2 | ≤0,25 | ≤0,2 | ≤0,01 | ≤0,1 | ≥220 | ≥110 | ≥6 | ≥70 | 9 |
Excellent friction qualities and good self-lubricating power. Used under difficult entrant conditions. Low lubrication. Speed <10 M / S. Allowable load 25 MPa. CuPb10Sn10Ni3 on request.
Bearings, friction plates.
-
15
-
CuPb15Sn7
-
CuPb15Sn8
Norms CC496K, EN 1982
Production technique Continous casting, Centrifugal casting
Chemical composition | Mechanical characteristics | ||||||||||||||||||||||||||||
Cu | Sn | Pb | Zn | P | Al | Ni | Fe | Mn | Si | Other | Rm | Rp | A% | HB | Density | ||||||||||||||
Reste | 6,0-8,0 | 13-17 | ≤2 | ≤0,1 | ≤0,01 | 0,5-2 | ≤0,25 | ≤0,2 | ≤0,01 | ≤0,1 | ≥200 | ≥90 | ≥7 | ≥65 | 9.1 |
Excellent friction properties even in case of imperfect lubrication. Recommended for frequent starts and stops. Low lubrication. Speed <14M / S. Allowable load 10 MPa.
Bearings, plastic injection.
-
20
-
CuPb20Sn5
Norms CC497K, EN 1982, NFA 53707
Production technique Continous casting, Centrifugal casting
Chemical composition | Mechanical characteristics | ||||||||||||||||||||||||||||
Cu | Sn | Pb | Zn | P | Al | Ni | Fe | Mn | Si | Other | Rm | Rp | A% | HB | Density | ||||||||||||||
Reste | 4,0-6,0 | 18-23 | ≤2 | ≤0,1 | ≤0,01 | 0,5-2,5 | ≤0,25 | ≤0,2 | ≤0,01 | ≤0,1 | ≥170 | ≥80 | ≥6 | ≥80 | 9.3 |
Excellent friction properties even in case of imperfect lubrication. Recommended for frequent starts and stops. Low lubrication. Speed <14M / S. Allowable load 10 MPa.
Bearings